Mmekọrịta Ngwongwo Ọdịdị PTFE

Ụzọ isi ghọta mmetụta nke fluorine bụ ịchọpụta ọdịiche dị n'etiti linear polyethylene (PE) na PTFE nke bụ fluoropolymer kacha elu n'ihe gbasara ihe na njirimara.

Enwere ọdịiche dị mkpa n'etiti njirimara PE na nke PTFE:

• * PTFE bụ otu n'ime polymer ike elu kacha ala
• *PTFE bụ polymer kachasị na-eguzogide ọgwụ
• *PTFE bụ otu n'ime polymer kwụsiri ike nke ọma
• *Ebe mgbaze na ike ndọda nke PTFE karịrị okpukpu abụọ nke polyethylene

PTFE na PE dị iche bụ nke a na-enweta na ọdịiche nke agbụ CeF na CeH.Ọdịiche dị na akụrụngwa eletrọnịkị na nha F na H na-eduga na nlebanya ndị a:

• *F bụ ihe kacha eletrọnịkị nke ihe niile (4 Paulings)
• *F nwere ụzọ abụọ eletrọn na-ekekọrịtaghị
• *F na-agbanwe ngwa ngwa ka ọ bụrụ Fe
• *Ike nkekọ nke CeF dị elu karịa CeH
• *F karịrị H

The electronegativity nke carbon na 2.5 Paulings dịtụ elu karịa nke hydrogen na ala karịa electronegativity nke fluorine.N'ihi ya, polarity nke njikọ CeF dị iche na nke njikọ CeH, na njikọ CeF na-agbakọ nke ukwuu.Na njikọ CeF, a na-ebo njedebe fluorine nke njikọ ahụ n'ụzọ na-adịghị mma ma e jiri ya tụnyere njikọ CeH nke a na-ebubo carbon na-adịghị mma.

Ọdịiche dị na polarity nke CeH na CeF na-emetụta nkwụsi ike nke nkwụsi ike nke ụdọ polymer abụọ ahụ.Crystallization nke polyethylene na-ewere ọnọdụ na atụmatụ na trans conformation.Enwere ike ịmanye PTFE n'ime mgbanwe dị otú ahụ na nrụgide dị oke elu.PTFE, n'okpuru 19 C, crystallizes dị ka helix nwere 0.169 nm kwa ugboro ugboro: ọ na-ewe 13 C atọm maka 180 ntụgharị ka emecha.N'elu 19 C, anya nkwugharị na-abawanye ruo 0.195 nm nke pụtara na a chọrọ carbon carbon 15 maka ntụgharị 180.N'elu 19 C, agbụ ahụ nwere ike ịkwaga n'akụkụ, nke na-abawanye n'elu 30 C ruo mgbe ọ ruru ebe mgbaze (327 C).

Ngbanwe nke F maka H na njikọ CeH na-abawanye ike nkekọ site na 99.5 kcal/mole maka njikọ CeH gaa na 116 kcal/mole maka njikọ CeF.N'ihi ya, nkwụsi ike okpomọkụ na nguzogide kemịkalụ nke PTFE dị elu karịa PE n'ihi na achọrọ ike ka ukwuu iji mebie njikọ CeF.Polarity na ike nke njikọ CeF na-eme ka F atom abstraction usoro maka ike alaka.N'ụzọ dị iche, polyethylene nwere alaka nke ukwuu (> alaka 8 kwa 100 carbon carbon) nwere ike ịmekọrịta.Usoro alaka dị ka ngwá ọrụ iji dozie kristal adịghị mma maka PTFE.Kama nke ahụ, ndị comonomers nwere otu pendent ga-eji TFE mee ihe.

Crystallinity nke PTFE na-agbazebeghị dị na nso nke 92e98%, na-agbanwe agbanwe na usoro agbụ na-enweghị alaka.FEP, onye copolymer nke TFE na HFP, nwere crystallinity dị ka-polymerized nke 40e50%.Na FEP, pendent CF3 otu na-ejikọta ya na carbon atọ nke na-adịchaghị nke ọma karịa carbon carbon nke mbụ na nke abụọ.Ọkpụkpụ mkpọda na-egosi nbibi okpomọkụ mmalite nke 300 C maka FEP (0.02% arọ ọnwụ) na 425 C maka PTFE (0.03% arọ ọnwụ).